EZ-Mix® 40
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | EZ-Mix® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pdxbYw_EZ-Mix-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EZ-MIX® 40 is a brushable polyurethane rubber mold compound that mixes and applies easily. Two liquids (Part A and Part B) are measured and combined in equal amounts by volume (no scale is necessary). After a few minutes of mixing, EZ-MIX® 40 is ready to be applied to a vertical surface with a brush. After a suitable thickness is attained (multiple layers), EZ-MIX® 40 cures overnight with negligible shrinkage to a flexible, durable mold rubber. Following the application of a support shell, a rubber mold made with EZ-MIX® 40 is suitable for casting a variety of materials including wax, gypsum, urethane/epoxy resins, concrete, cement, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.975 | cm³/g | ASTM D1475 |
| Viscosity | Brushable | ASTM D2393 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 100A:85B by weight 1A:1B by volume |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | < 0.10 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 40 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 2.90 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 580 | % | ASTM D412 |
| Tear Strength 1 | 11.7 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 18 | min | ASTM D2471 |
| Demold Time (23°C) | 960 | min |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PA540G30N | Guangdong Silver Age Sci & Tech. Co., Ltd | Nylon 6 | SILVER® |
| TOTAL Polypropylene PPH 3827WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| ENVIROPLAS® ENV13-NC230 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |
| POTICON OA20 | Otsuka Chemical Co., Ltd. | Acetal (POM) Copolymer | POTICON |
| LNP™ LUBRICOMP™ DCP32 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |