Karina BLACK PVC COMPOUND 90850-48/ 1-D-AC-HSF
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pdrNmm_Karina-BLACK-PVC-COMPOUND-90850-48-1-D-AC-HSF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE AND FLAME RETARDANT PVC COMPOUND RECOMMENDED FOR INSULATION AND JACKET (ST2) OF CABLES CLASS 90C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 to 1.46 | g/cm³ | IEC 60811-1-3 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -0.880 to 0.720 | ME 12 | |
| Color b | -1.23 to 0.370 | ME 12 | |
| Color L | 26.9 to 28.5 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 86 to 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 14.7 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 200 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 10.3 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 130 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 30 | % | NBR 6245 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 121°C |
| 3 . | Aged in Air for 168 hr at 121°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-115A | Teknor Apex Company | TPE | Medalist® |
| Shanghai Ofluorine PVDF T-1 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| TORZEN® U4664FL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Unichem 6576 | Colorite Polymers | PVC, Unspecified | Unichem |
| KER® 1739 | Synthos S.A. | SBR, Emulsion | KER® |