Order Products : sales@su-jiao.com
Sipolprene® 35150
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SIPOL S.p.A |
| Trademark: | Sipolprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pceRTv_Sipolprene-35150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sipolprene® 35150 is an ether ester thermoplastic elastomer (TPC-ET), developed and manufactured by Sipol, with a nominal hardness of Shore D 36, a low modulus, and a rheological behaviour, which makes it suitable for injection molding and extrusion processing. Sipolprene® 35150 has been specifically developed with a low melting point which make it suitable for blending with PVC to make soft compounds plasticizer free. Sipolprene® 35150 comes in a natural color with a standard stabilisation package fully in compliance with American FDA and European EU 10/2011 Food Contact Regulations. Black color and/or UV stabilised and/or heat stabilised are all available in dry blend version on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.90 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 36 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 28.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 600 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 40.0 | MPa | ASTM D790, ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 100 | kN/m | ASTM D1004 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ISO 306/A50, ASTM D1525 1 |
| Peak Melting Temperature | 150 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6300HJ | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| VALOX™ VX5011 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| Celstran® +PP-GF40-04CN03 | Celanese Corporation | PP, Unspecified | Celstran® |
| FLEXAREN® 07000 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| E-RIALFILL H 07 55 C | RIALTI Srl | PP Homopolymer | E-RIALFILL |