CRYSTALADD® HM-237B

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Ravago Manufacturing Americas, LLC
Trademark:	CRYSTALADD®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	pcVmNF_CRYSTALADD-HM-237B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
NUCLEATOR MASTERBATCH HM-237B is an additive concentrate containing a highly efficient Nucleator. Nucleation in LLDPE can improve film properties, clarity, barrier and yield rates. In blow molding for PE, HM-237B can reduce cycle time and achieve better control over shrinkage characteristics. In injection molding applications the nucleator will provide faster cycle times, lower shrinkage and higher barrier properties. Key Features: Designed to be added to polyethylene film, extrusion, blow molding and injection molding resins. Improved clarity in films, bottles and injection molded articles Uniform concentration of additives in concentrate form. Masterbatch pellet form for ease of addition and feeding into extrusion equipment Directions for Use: HM-237B is added to HDPE, LDPE or LLDPE at 2.5% to achieve improved crystallization for faster cooling, lower warpage especially between different colors. Achieve more uniform crystal sizes as the PE cools for improved gloss and barrier properties along with excellent clarity. Note: Effectiveness reduced in LDPE with molecular weights resulting in < 2.0 MI or high LCB. FDA Compliance: The components of this product are compliant with FDA requirements up to 9% LD by weight. Please consult with the FDA regulations for specific application requirements. This product has a Drug Master File (DMF) listing.

Message

NUCLEATOR MASTERBATCH

HM-237B is an additive concentrate containing a highly efficient Nucleator. Nucleation in LLDPE can improve film properties, clarity, barrier and yield rates. In blow molding for PE, HM-237B can reduce cycle time and achieve better control over shrinkage characteristics. In injection molding applications the nucleator will provide faster cycle times, lower shrinkage and higher barrier properties.

Key Features:

Designed to be added to polyethylene film, extrusion, blow molding and injection molding resins.

Improved clarity in films, bottles and injection molded articles

Uniform concentration of additives in concentrate form.

Masterbatch pellet form for ease of addition and feeding into extrusion equipment

Directions for Use:

HM-237B is added to HDPE, LDPE or LLDPE at 2.5% to achieve improved crystallization for faster cooling, lower warpage especially between different colors. Achieve more uniform crystal sizes as the PE cools for improved gloss and barrier properties along with excellent clarity.

Note: Effectiveness reduced in LDPE with molecular weights resulting in < 2.0 MI or high LCB.

FDA Compliance:

The components of this product are compliant with FDA requirements up to 9% LD by weight. Please consult with the FDA regulations for specific application requirements.

This product has a Drug Master File (DMF) listing.

General Information
Additive	Nucleating Agent
Features	Nucleated
Uses	Masterbatch
Agency Ratings	DMF Unspecified Rating FDA Unspecified Rating
Forms	Pellets
Processing Method	Blow Molding Extrusion Film Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.920	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	5.2	g/10 min	ASTM D1238

Additional Information	Nominal Value	Unit	Test Method
Nucleating Agent	4.0	%	Internal Method
Polymer Base	LLDPE

Resin Grade	Manufacturer	Category	Trademark
ARCEL® 730 (2.00 pcf)	NOVA Chemicals	PS+PE	ARCEL®
Chemlon® 104 HU	Teknor Apex Company (Chem Polymer)	Nylon 66	Chemlon®
Duratuf™ 830U2/X	Technical Polymers, LLC	Acetal (POM) Copolymer	Duratuf™
ELASTOSIL® LR 3003/70 A/B	Wacker Chemie AG	Silicone	ELASTOSIL® LR
Sylvin 86019-80 Clear	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin