Plexiglas® Resist zk6HC

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	pa6b1S_Plexiglas-Resist-zk6HC.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Profile:
PLEXIGLAS® Resist zk6HC is an amorphous, impact-modified thermoplastic molding compounds (PMMA-I).

Typical properties of impact-modified PLEXIGLAS® molding compounds are

high weather resistance

excellent transmission and clarity

brilliant appearance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk6HC is characterized by the following special properties:

excellent break resistance and impact strength

best resistance to stress cracking of all impact-modified PLEXIGLAS® molding compounds.

Application:
Used for extruding and coextruding sheets and profiles

Examples:
extruded/coextruded sheets and profiles for automotive bodies and the sanitaryware sector (bathtubs and shower trays) or crystal-clear luminaire covers for industrial plants that come into contact with aggressive media.

General Information
Additive	Impact Modifier
Features	Good Weather Resistance High Clarity High ESCR (Stress Crack Resist.) High Impact Resistance Pleasing Surface Appearance
Uses	Automotive Applications Automotive Bumper Automotive Exterior Parts Automotive Exterior Trim Profiles Protective Coverings Sanitary Products Sheet
Forms	Pellets
Processing Method	Coextrusion Extrusion
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.16	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	0.400	cm³/10min	ISO 1133
Water Absorption			ISO 62
23°C, 24 hr	1.8	%
Equilibrium, 23°C, 50% RH	0.50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2000	MPa	ISO 527-2/1
Tensile Stress (Yield)	47.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	5.5	%	ISO 527-2/50
Nominal Tensile Strain at Break	48	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	80	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	97.0	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	1.1E-4	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	91.0	%	ISO 13468-2

Extrusion	Nominal Value	Unit
Drying Temperature	< 85.0	°C
Drying Time	2.0 to 3.0	hr
Melt Temperature	220 to 260	°C
Die Temperature	220 to 260	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
Mowital® B 60 T	Kuraray Co., Ltd.	PVB	Mowital®
Ultramid® 8202C HS	BASF Corporation	Nylon 6	Ultramid®
Zhongfa PP GR-30H	Yuyao Zhongfa Engineering Plastics Co. Ltd.	PP, Unspecified	Zhongfa
ACCUTECH™ HP0334W20L1	ACLO Compounders Inc.	PP Homopolymer	ACCUTECH™
EMOPLEN® CP GFR 20	EMAS Plastik San.Tic.AS.	PP Copolymer	EMOPLEN®