LNP™ THERMOCOMP™ DX06409 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pZ4tMI_LNPTHERMOCOMPDX06409compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DX06409 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release. Also known as: LNP* THERMOCOMP* Compound DF-1002 EM MR HC Product reorder name: DX06409 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.28 | g/cm³ | ASTM D792 |
| -- | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.51 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.43 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4170 | MPa | ASTM D638 |
| -- | 4100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 83.4 | MPa | ASTM D638 |
| Fracture | 84.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 3.8 | % | ASTM D638 |
| Fracture | 3.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4280 | MPa | ASTM D790 |
| -- | 3920 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 145 | MPa | ASTM D790 |
| -- | 117 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 8.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 910 | J/m | ASTM D4812 |
| 23°C 3 | 62 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.0 | J | ASTM D3763 |
| -- | 9.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 141 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 137 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 5.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm, Testing by SABIC) | V-1 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9120 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| LIHAN® A9705EP | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| Karina IVORY PVC COMPOUND -E 854-35/ 9-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® NA205000 | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 4299-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |