LNP™ THERMOCOMP™ RF007ES compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pXmug0_LNP-THERMOCOMP-RF007ES-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF007ES is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Easy Molding. Also known as: LNP* THERMOCOMP* Compound RF-1007 EM HS Product reorder name: RF007ES |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.41 | g/cm³ | |
| -- | 1.40 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.90 to 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.84 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10700 | MPa | ASTM D638 |
| -- | 10300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 152 | MPa | ASTM D638 |
| Yield | 149 | MPa | ISO 527-2/5 |
| Break 3 | 151 | MPa | ASTM D638 |
| Break | 149 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.4 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2/5 |
| Break 5 | 2.5 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 9320 | MPa | ASTM D790 |
| -- 7 | 9060 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 220 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 227 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 226 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 62 | J/m | ASTM D256 |
| 23°C 10 | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D4812 |
| 23°C 11 | 41 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.08 | J | ASTM D3763 |
| -- | 2.86 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 255 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 252 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 237 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 228 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RoyalEdge® 5030 | Lion Copolymer, LLC | EPDM | RoyalEdge® |
| TOTAL Polypropylene PPC 10641 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Axiall PVC 8424 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Edgetek™ PF-20GF/000 | PolyOne Corporation | PSU | Edgetek™ |
| LG PS 65IHE | LG Chem Ltd. | PS (HIPS) | LG PS |