Novamid® ES110C
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Novamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pX17GL_Novamid-ES110C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novamid® ES110C is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific for injection molding. Primary attribute of Novamid® ES110C: Good Processability. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.3 | % | |
| Flow | 1.1 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.8 | % | ISO 62 |
| Viscosity Number | 118 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 84.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 18 | % | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Stress | 114 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.1 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 173 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 76.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 88X-D | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| APEX® 6500-75 | Teknor Apex Company | PVC, Flexible | APEX® |
| Flontech® FT-M02-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| KumhoSunny ABS H2938Z | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Pearlbond™ 120 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |