TRANSMARE® 19HGF40-1.003
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pWyvsD_TRANSMARE-19HGF40-1-003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 19HGF40-1.003 is a 40% glass fibre reinforced polypropylene homopolymer for injection moulding purposes with very high stiffness and good flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 4.5 | g/10 min | |
| 230°C/5.0 kg | 18 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 4.00 mm) | 120 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 8750 | MPa | ISO 178 |
| Flexural Stress 2 | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -40°C | 8.5 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 10 | kJ/m² | |
| 23°C | 13 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 156 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 144 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 161 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIVIC® 2870 | SIDIAC | PVC+NBR | SIVIC® |
| Moplen EP440G | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| DynaChar™ 2436-TH | Polymer Dynamix | TPU, Unspecified | DynaChar™ |
| Dynaflex™ G2709-1000-00 | PolyOne Corporation | TPE | Dynaflex™ |
| Sylvin 8344-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |