Tecotek® PC40 NL VB02
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecotek® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pW5Fsu_Tecotek-PC40-NL-VB02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/PBT, unfilled, UV stabilized, high impact, natural |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.0 | % | |
| Flow | 1.0 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 0.10 | % | ISO 960 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2250 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | > 50 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 to 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Battery GPP6100-116C | S&E Specialty Polymers, LLC | TPO | S&E Battery |
| Microthene® F FE53200 | LyondellBasell Industries | EVA | Microthene® F |
| Wanthane® WHT-1180 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Electrafil® PA6/6 GF13 SS10 BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| HiFill® PA12 GF50 L | Techmer Engineered Solutions | Nylon 12 | HiFill® |