Rilsan® BESNO P20 TL
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pT5Tnc_Rilsan-BESNO-P20-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BESNO P20 TL is a polyamide 11 produced from a renewable source. This natural grade is plasticized and designed for extrusion MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 72 | ||
| Shore D, 15 sec | 66 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 520 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 54.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 200 | % | ISO 527-2 |
| Flexural Modulus | 460 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 10 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 182 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11-P, EHL, 22-003 | ISO 1874 | |
| Renewable Carbon Conent | > 93 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 230 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP110-13-45 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Viton® GBL-200S | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| APTIV® 2000 | Victrex plc | PEEK | APTIV® |
| K-Prene SHEATHING EPR 5064 | Technovinyl Polymers India Ltd. | MPR | K-Prene |
| KRATON® D3226 DI | Kraton Polymers LLC | SBS | KRATON® |