ALCOM® LB PC 1000 14073 WT1164-14
| Category: | PC , Polycarbonate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® LB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pSVUIG_ALCOMLBPC100014073WT116414.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM®LB PC 1000 14073 WT1164-14 is a polycarbonate (PC) product containing filler. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. ALCOM®The application fields of LB PC 1000 14073 WT1164-14 include reflector, automobile industry and lighting equipment. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 35.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 20 | % | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% strain | 76.0 | MPa | ISO 178 |
| -- | 100 | MPa | ISO 178 |
| Flexural Deflection at Max Force | 7.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 95 | % | DIN 5033 |
| Y10 of Transmission : 500.0 µm | 3.0 | % | ISO 13468 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 137 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 100 - 120 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 - 320 | °C | |
| Mold Temperature | 80 - 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylex™ 1230 | Multibase, A Dow Corning Company | Nylon+PP | Nylex™ |
| Bergadur™ PB40 G20 NC012 | PolyOne Corporation | PBT | Bergadur™ |
| APEX® 1564 | Teknor Apex Company | PVC, Flexible | APEX® |
| Ateva® 1241 | Celanese EVA Performance Polymers | EVA | Ateva® |
| ICORENE® 8040 WS | ICO Polymers EMEA, A Division of A. Schulman | HDPE | ICORENE® |