ASTALOY™ PC/ABS M130GF10
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pSRRGU_ASTALOY-PC-ABS-M130GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALOY™ PC/ABS M130GF10 is a high melt flow 10% glass filled alloy of ABS and Polycarbonate and is designed for long flow path injection moulding applications requiring a balance of product rigidity, product toughness, high heat and creep resistance with a minimal expansion of moulded product under heating. Typical applications include automotive instrument panel retainer assemblies and painted exterior body panels. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/3.8 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 56.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 8.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3300 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 103 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 107 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 112 | °C | |
| Vicat Softening Temperature | 132 | °C | ASTM D1525 5 |
| CLTE - Flow | 3.9E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 235 to 255 | °C | |
| Middle Temperature | 245 to 265 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6413-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unichem 7011-Rad | Colorite Polymers | PVC, Unspecified | Unichem |
| Adell PP EF-32 | Adell Plastics, Inc. | PP, Unspecified | Adell PP |
| Hypro® PP-HP 20NS | Entec Polymers | PP Homopolymer | Hypro® |
| Eltex® PF6212KE | INEOS Olefins & Polymers Europe | mLLDPE | Eltex® |