LNP™ THERMOCOMP™ IX04513C compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pPTlCs_LNP-THERMOCOMP-IX04513C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System. Also known as: LNP* THERMOCOMP* Compound PDX-I-04513 CCS Product reorder name: IX04513C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.90 to 1.1 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.21 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8840 | MPa | ASTM D638 |
| -- | 8290 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 131 | MPa | ASTM D638 |
| Break | 128 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.3 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8080 | MPa | ASTM D790 |
| -- | 7110 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 204 | MPa | ASTM D790 |
| -- | 187 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 690 | J/m | ASTM D4812 |
| 23°C 3 | 42 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.2 | J | ASTM D3763 |
| -- | 3.06 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 197 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 192 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Valtec HS020FM | INDELPRO, S.A. de C.V. | PP Homopolymer | Valtec |
| CERTENE™ PBM-20N | Muehlstein | PP Impact Copolymer | CERTENE™ |
| GELOY™ XTWE270M resin | SABIC Innovative Plastics Asia Pacific | ASA+SAN | GELOY™ |
| Grilamid® LBV-65H FWA black 9225 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| K-Resin® SBC KR52 | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |