VAMPSAB 023 V0 AF
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPSAB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pOrYAZ_VAMPSAB-023-V0-AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0, high fluidity, good impact strenght. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.80 | % | |
| Across Flow | 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 10 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 1 |
| RTI Elec | 70.0 | °C | UL 746 |
| RTI Imp | 70.0 | °C | UL 746 |
| RTI Str | 70.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 | °C | |
| Mold Temperature | 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viton® AL-300 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| TufCoat™ 4600 | Lucite International Inc. | Acrylic (PMMA) | TufCoat™ |
| BJB Polyurethane SP-301 A/B-4 | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Huafon HF-3380A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Hostacom SP 98/E/96 | LyondellBasell Industries | PP Copolymer | Hostacom |