PELPRENE™ S2002
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PELPRENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pO2Tqf_PELPRENE-S2002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PELPRENE™ S2002 is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.3 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.38 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A | 97 | JIS K6301 | |
| Shore D | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 38.0 | MPa | |
| 50% Strain | 16.7 | MPa | |
| Tensile Elongation (Break) | 550 | % | ASTM D638 |
| Flexural Modulus | 206 | MPa | ASTM D790 |
| Compressive Strength (10% Strain) | 16.3 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 12.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 155 | kN/m | ASTM D624 |
| Compression Set | 61 | % | JIS K6301 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 107 | °C | ASTM D648 |
| Brittleness Temperature | < -65.0 | °C | JIS K6301 |
| Vicat Softening Temperature | 185 | °C | ASTM D1525 |
| Melting Temperature | 206 | °C | DSC |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | JIS K2111 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resilience | 60 | % | JIS K6301 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8744 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Ultraform® N 2320 003 BK120 Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Algoflon® L600 | Solvay Specialty Polymers | PTFE | Algoflon® |
| INSTRUC PEGF10 | Infinity LTL Engineered Compounds | PE, Unspecified | INSTRUC |
| MAJORIS DFR150 | AD majoris | PP, Unspecified | MAJORIS |