Durethan® BKV 230 H2.0 DUS008 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pLhSiN_Durethan-BKV-230-H2-0-DUS008-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.85 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.14 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.35 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.040 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8600 | 4400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.5 | 8.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 7500 | 4400 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 205 | 105 | MPa | |
| 23°C 6 | 210 | 125 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 4.5 | 6.2 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6-HI, GHR, 14-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 14 | 15 | kJ/m² | |
| 23°C | 23 | 35 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 75 | 75 | kJ/m² | |
| 23°C | 75 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 218 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 198 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW1701 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| Niche ABSN4BK | Niche Polymer, LLC | ABS | Niche |
| Hostaform® C 9021 M XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LNP™ STAT-KON™ DX04403 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| ACRYPET® VH5 | Lucite International Holland BV | Acrylic (PMMA) | ACRYPET® |