NYLOY® MG-8030N-V 60BK1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pLWRLc_NYLOY-MG-8030N-V-60BK1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYLOY® MG-8030N-V 60BK1 is a Polyamide 66 (Nylon 66) material filled with 34% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of NYLOY® MG-8030N-V 60BK1 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.24 | g/cm³ | ASTM D792 |
| -- | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.38 | % | |
| Across Flow | 1.1 | % | |
| Ash Content | 35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 127 | MPa | ASTM D638 |
| -- | 120 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.3 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9420 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 181 | MPa | ASTM D790 |
| -- | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 235 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 230 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | > 2.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA66 43 GF BLK/BLK | RTP Company | Nylon 66 | RTP |
| Spartech Polycom SC2F-1090 | Spartech Polycom | PS (HIPS) | Spartech |
| Moplen HP527J | LyondellBasell Industries | PP Homopolymer | Moplen |
| Karina CRYSTAL CLEAR PVC COMPOUND -E 80/224-IS-SD-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PHOENIX™ 14701 | Phon Tech Industrial Company | TPE | PHOENIX™ |