AIE PPO 9010F-S120E
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE PPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pKTbeT_AIE-PPO-9010F-S120E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AIE PPO 9010F-S120E is a Polyphenylene Ether + PS (PPE+PS) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of AIE PPO 9010F-S120E: Flame Rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.70 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 68.0 | MPa | ISO 527-2/1/50 |
| Flexural Modulus | 2450 | MPa | ISO 178 |
| Flexural Stress | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 23 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 3.20 mm Span | 139 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm Span | 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 129 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-1 | ||
| 3.18 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 300 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Pressure | 30.0 to 80.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECASON™ P XRO | Ensinger Inc. | PPSU | TECASON™ |
| Wanthane® WHT-2198 | Wanhua Chemical Group Co., Ltd. | TPU-Capro | Wanthane® |
| Adflex Q 402 F | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |
| BMC T15(GP) | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Durez® 37081 | SBHPP | Phenolic | Durez® |