LNP™ THERMOCOMP™ LC003E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pKLs5A_LNPTHERMOCOMPLC003Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* LC003E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound LC-1003 EM Product reorder name: LC003E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 - 0.60 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.51 - 0.58 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.28 - 0.31 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11500 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 154 | MPa | ASTM D638 |
| Fracture | 163 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.8 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 9510 | MPa | ASTM D790 |
| -- | 9850 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 259 | MPa | ASTM D790 |
| -- | 263 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 4.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.40 | J | ASTM D3763 |
| -- | 1.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 270 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 298 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 5.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+7 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 - 360 | °C | |
| Middle Temperature | 366 - 377 | °C | |
| Front Temperature | 382 - 393 | °C | |
| Processing (Melt) Temp | 382 - 388 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Surlyn® 1601 | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| WELLAMID Nylon 6600 GV 25 DHCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| ZELAS® MC642 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | ZELAS® |
| Hostaform® C 27021 TF | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LNP™ LUBRICOMP™ XFL21R compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ LUBRICOMP™ |