Maxxam™ PPR 40G BK701
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pKGBr9_Maxxam-PPR-40G-BK701.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Maxxam™PPR 40G BK701 is a polypropylene product, and the filler is glass fiber reinforced material. It can be processed by injection molding and is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 90.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 6500 | MPa | ASTM D790 |
| Flexural Strength 3 | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 145 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 200 - 240 | °C | |
| Middle Temperature | 200 - 240 | °C | |
| Front Temperature | 200 - 240 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® D natural | Röchling Engineering Plastics SE & Co. KG | HMWPE | POLYSTONE® |
| TEREZ PA 6.6 7500 GF 15 GK 15 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Dyna-Purge® X | Dyna-Purge, division of Shuman Plastics | Proprietary | Dyna-Purge® |
| Karina WHITE COLOR CONCNETRATE 10/ 92-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Rotuba CAB B932 (4% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |