Ultramid® B3WG13 BK00102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pGrX3v_Ultramid-B3WG13-BK00102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3WG13 BK00102 is a 63% glass reinforced, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldability and outstanding surface appearance. Potential applications are mirror brackets, fuel lids, gas-assisted steering wheel inserts, ski bindings and bike rack clamps. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.74 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 22000 | 13400 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 207 | -- | MPa | ASTM D638 |
| Break, 23°C | 235 | 155 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 3.0 | -- | % | ASTM D638 |
| Break, 23°C | 2.0 | -- | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 17300 | -- | MPa | ASTM D790 |
| 23°C | 19000 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 378 | -- | MPa | ASTM D790 |
| 23°C | 355 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 13 | -- | kJ/m² | |
| 23°C | 15 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 90 | -- | kJ/m² | |
| 23°C | 90 | -- | kJ/m² | |
| Notched Izod Impact | ||||
| 23°C | 160 | -- | J/m | ASTM D256 |
| 23°C | 15 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 1.8 MPa, Unannealed | 213 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 214 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| RTI Elec | UL 746 | |||
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 110 | -- | °C | |
| RTI Str | UL 746 | |||
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 275 to 300 | °C | |
| Middle Temperature | 285 to 310 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 300 to 320 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zythane® 5080A | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Axiall PVC 16902 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| China PPS hGR30 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Durolon® V2600 | Unigel Plásticos | PC | Durolon® |
| LNP™ LUBRICOMP™ WFL36 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |