Sumikon® PM-9840
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pGhsme_SumikonPM9840.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® PM-9840 (Type J Black) is Glass fiber , Inorganic filler and Organic fiber filled resol resin (non-anmonia phenolic) molding compound with good mechanical property and heat resistance. This grade is official registered UL with V-0 (t=0.17). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.75 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.26 | % | JIS K6911 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 74.0 | MPa | JIS K6911 |
| Flexural Modulus | 7300 | MPa | JIS K6911 |
| Flexural Strength | 106 | MPa | JIS K6911 |
| Compressive Strength | 209 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.2 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 202 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 9.0 | kV/mm | JIS K6911 |
| Arc Resistance | 149 | sec | JIS K6911 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 2.0E+11 | ohms | JIS K6911 |
| -- 3 | 2.0E+10 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.170 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 9020 HS | PolyPacific Pty. Ltd. | PP Homopolymer | Retpol® |
| TEREZ PA 6.6 HT 7110 GF 41 FL-HF/2 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Karina BEIGE PVC COMPOUND -E 898-08/175-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1700-8126 | Lehmann & Voss & Co. | PPE | LUVOCOM® |
| Sylvin 8485-60 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |