LIHAN® A9705PBK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pFiqSp_LIHAN-A9705PBK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LIHAN® A9705PBK is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.40 to 0.80 | -- | % | ISO 62 |
| Water Content | 5.5 to 6.5 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 115 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 130 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7000 | -- | MPa | ISO 178 |
| Flexural Stress | 180 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 13 | 16 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | DSC |
| CLTE - Flow | 2.5E-5 to 3.5E-5 | 6.0E-5 to 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | ASTM D257 |
| Dielectric Strength | 17 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J-2000GP | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Moplen HP601J | LyondellBasell Industries | PP Homopolymer | Moplen |
| TITANLENE® LDF 200GG | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Borealis PE FG5223 | Borealis AG | LLDPE | Borealis PE |
| Sinvicomp SIM10530 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | SINVICOMP |