HiFill® PEEK GF30 HT011A
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pF7WDo_HiFill-PEEK-GF30-HT011A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PEEK GF30 HT011A is a Polyetheretherketone (PEEK) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -- 2 | 12200 | MPa | |
| -- | 10900 | MPa | |
| Tensile Strength | ASTM D638 | ||
| Break 3 | 178 | MPa | |
| Break | 157 | MPa | |
| Tensile Elongation 4(Break) | 3.9 3.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Flexural Strength | 217 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -- 5 | 99 | J/m | |
| 23°C, 3.18 mm | 93 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 316 | °C | ASTM D648 |
| Melting Temperature | 342 | °C | |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 6 | 23 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Annealed |
| 2 . | Annealed Data 200C, 4 Hours |
| 3 . | Annealed Data 200C, 4 Hours |
| 4 . | Annealed Data 200C, 4 Hours |
| 5 . | Annealed Data 200C, 4 Hours |
| 6 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1800 A | RTP Company | PC+Acrylic | RTP |
| Borealis PP HG455FB | Borealis AG | PP Homopolymer | Borealis PP |
| Ferro PP TPP10AN52NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Ferro PP NPP00GX08BK | Ferro Corporation | Polyolefin, Unspecified | Ferro PP |
| Sylvin 4260-65FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |