Toppyl SP 2000 B
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Toppyl |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pEpKcC_Toppyl-SP-2000-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toppyl SP 2000 B is a fully formulated seal peel solution especially developed for the blown film technology. This product has been designed to offer a peelable seal to PE substrates or to seal & peel against itself and is suitable for non-sterilisable applications. Toppyl SP 2000B is a solution created to replace completely the sealing layer in a coextruded film. It provides a constant easy-opening force over a wide sealing temperature window and is readily processable on conventional equipment in both mono and co-extruded structures. EU and FDA compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.912 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD | 185 | MPa | ASTM D882 |
| Tensile Strength - MD | ASTM D882 | ||
| Yield | 9.00 | MPa | |
| Break | 28.0 | MPa | |
| Tensile Elongation - MD (Break) | 670 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/A50 |
| Melting Temperature | 110 | °C | DSC |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EXCEVAL™ HR-3010 | Kuraray Co., Ltd. | EVA | EXCEVAL™ |
| Fluoroelastomer 931 | Greene, Tweed & Co. | Fluorelastomer | Fluoroelastomer |
| TOTAL Polypropylene Lumicene® MH 140CN0 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| LUVOTECH® MR 2007/BL | LEHVOSS Group | Nylon 6 | LUVOTECH® |
| DAI-EL™ T-530 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |