Complet® LCF30-TPU
| Category: | ETPU , Engineering Thermoplastic Polyurethane |
| Manufacturer: | PlastiComp, Inc. |
| Trademark: | Complet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pEe99U_Complet-LCF30-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Complet®LCF30-TPU is an engineering thermoplastic polyurethane (ETPU) product, which contains 30% long carbon fiber as filler. It is available in North America, Europe or Asia Pacific. The main features are: Rohs certification. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 24900 | MPa | ASTM D638 |
| Tensile Strength | 269 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 17900 | MPa | ASTM D790 |
| Flexural Strength | 389 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 190 | J/m | ASTM D256 |
| Unnotched Izod Impact | 830 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 204 - 227 | °C | |
| Middle Temperature | 210 - 232 | °C | |
| Front Temperature | 216 - 238 | °C | |
| Nozzle Temperature | 221 - 243 | °C | |
| Processing (Melt) Temp | 216 - 238 | °C | |
| Mold Temperature | 87.8 | °C | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 30 - 50 | rpm | |
| Cushion | 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Injection speed: 2 to 3 in/secInjection pressure: medium to maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® C-408 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Versollan™ RU 2205-1 | PolyOne Corporation | TPE | Versollan™ |
| WELLAMID Nylon 6600 GV 40 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| LNP™ STAT-KON™ DX09315C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| ADENE® N09CTE-00 | A.D. Compound S.p.A. | PP Homopolymer | ADENE® |