Durez® 118 (Injection)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Durez® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pDzGfy_Durez-118-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Durez 118 Black Phenolic is a two-stage, general purpose molding material. It exhibits improved impact strength and resistance to flexural fatigue for demanding automotive, electrical and appliance applications. Shrinkage and mechanical strengths are closely controlled to meet part reliability requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Apparent Density | 0.58 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 1.1 | % | ASTM D6289 |
| Water Absorption | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8300 | MPa | ASTM D638 |
| Tensile Strength | 48.0 | MPa | ASTM D638 |
| Flexural Strength | 69.0 | MPa | ASTM D790 |
| Compressive Strength | 207 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 17 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 149 | °C | ASTM D648 |
| RTI Elec (3.00 mm) | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 8.9 | kV/mm | ASTM D149 |
| -- 2 | 6.9 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.50 | ASTM D2520 | |
| Dissipation Factor (1 MHz) | 0.060 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | V-1 | UL 94 | |
| 6.00 mm | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life | 52 | wk |
| Additional Information |
|---|
| Test Specimens Molded at 340-350°FTypical transfer-molded shrinkage is 0.009 in/in |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymist® XPP 548 | Solvay Specialty Polymers | PTFE | Polymist® |
| Epoxies, Ect. 50-1225 | Epoxies, Etc. | Silicone | Epoxies, Ect. |
| LNP™ THERMOCOMP™ UF007AS compound | SABIC Innovative Plastics Europe | PPA | LNP™ THERMOCOMP™ |
| LOXIM 230 01 HB | LOXIM Industries Private Limited | PBT | LOXIM |
| SHINSTRA WG33TKB | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |