Shinko-Lac® ABS 7001
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pDa2zz_Shinko-Lac-ABS-7001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS 7001 is a standard grade of ABS that features high impact resistance along with an excellent balance of rigidity, strength, processability and glossiness. Typical applications of 7001 include furniture material, automotive parts, bobbin and refrigerator pockets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2160 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 38.2 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 61.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 130 | J/m | ASTM D256 |
| 0°C, 6.35 mm | 260 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 90.0 | °C | ASTM D648 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4565 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| NORYL GTX鈩?GTX679 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| NuSil CV1-1148 | NuSil Technology | Silicone | NuSil |
| Ateva® 2604A | Celanese EVA Performance Polymers | EVA | Ateva® |
| INTEGRATE™ NE542013 | LyondellBasell Industries | Polyolefin, Unspecified | INTEGRATE™ |