Next PC CXF-01NC
| Category: | PC , Polycarbonate |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pDCuDV_Next-PC-CXF-01NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PC UnFilled FR Natural Compound Product Applications Electrical/Electronics, Housing Appliance, Industrial, Medical & health care application, Telecommunication hardware, Capacitors, CDs, DVD, Compact discs, LCD, etc Benefits Good dimensional stability & High heat resistance |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.50 | % | |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.30 | % | |
| Saturation 1 | 0.35 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638 |
| Tensile Strength | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 70 | % | ASTM D638 |
| Flexural Modulus | 2250 | MPa | ASTM D790 |
| Flexural Strength | 92.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) | ASTM D256 | ||
| -30°C | 12.0 | kJ/m² | |
| 23°C | 70.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Unannealed | 126 | °C | |
| Vicat Softening Temperature | 141 | °C | ASTM D1525 |
| CLTE - Flow (23 to 80°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 28 | kV/mm | IEC 60243-1 |
| Dielectric Constant (60 Hz) | 3.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 270 to 280 | °C | |
| Middle Temperature | 280 to 290 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 D TFE 5 | RTP Company | Nylon 612 | RTP |
| SWANCOR Epoxy 901-2T | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| FHR Polypropylene AP5155-HA | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| En Chuan 336 | En Chuan Chemical Industries Co,. Ltd. | PS (GPPS) | En Chuan |
| Braskem PP DR152.02 | Braskem Europe GmbH | PP Random Copolymer | Braskem PP |