GETILAN GPE/400 E
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pCY8ZG_GETILAN-GPE-400-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN is our trade-mark of our crosslinkable polythene. GETILAN GPE/400 E is a medium density chemically crosslinkable polythene for low and medium voltage power cable insulation and sheathing. It is a conveniently grafted polythene able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 or MAC/100 SCU red copper resistant. REACTION BETWEEN GRAFTING AND CATALYST: These two polythenes, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 4.0 - 5.0 | g/10 min | ASTM D1238 |
| Water absorption rate- 24 hr (100°C) | 6.00 | g/m² | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1(200°C) | -5.0 50 - 70 | % | IEC 60811 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 450 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | 8.0 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (135°C, 168 hr) | -13 | % | ISO 188 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | BS 6622 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 180 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Die Temperature | 200 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin into hot water at 85/90°C for two hours (up to 3 mm thickness). Steam treatment at 0.15 for bar 5/6 hours. Faster ambient curing is possible depending from the atmospheric conditions. |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ P80A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| FRIANYL® B3 VNGF25 V0 | Nilit Plastics | Nylon 6 | FRIANYL® |
| INEOS PP H03G-02 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| Sylvin 2946-75 White 1547 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ SLX1432 resin | SABIC Innovative Plastics | PC | LEXAN™ |