SABIC® LLDPE 118N

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Saudi Basic Industries Corporation (SABIC)
Trademark:	SABIC® LLDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	pAnu5n_SABIC-LLDPE-118N.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Wire and Cable:

SABIC® LLDPE 118N is a Linear Low Density Polyethylene natural resin designed for wire and cable applications. SABIC® LLDPE 118N contains a low level of antioxidants and does not contain any antiblock and/or slip agents. It also exhibits excellent Environmental Stress Crack Resistance (ESCR). Sufficient Cu-inhibitor should be added to meet specific ageing requirements. For jacketing applications, addition of Carbon Black or UV stabilizer is required.

Applications: Telecommunication and Power cable (LV, MV, HV) jacketing. Halogen-free flame retardant (HFFR) compounds.

Blown Film:

SABIC® LLDPE 118N is a butene linear low density polyethylene resin designed for general purpose applications. Films produced from this resin are tough with excellent puncture resistance, high tensile strength and good hottack properties.

Applications: Typical applications for SABIC® LLDPE 118N are shipping sacks, ice bags, frozen food bags, liners, carrier bags, garbage bags, agriculture films, lamination and coextruded films, shrink film (for blending with LDPE), industrial consumer packaging and high clarity film if blended with (10-20%) LDPE.

The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.

General Information
Additive	Antioxidation
Features	High ESCR (Stress Cracking Resistance) High tensile strength Perforation resistance Antioxidation Good toughness Compliance of Food Exposure General
Uses	Packaging Films Laminate Lining Bags Cable sheath Wire and cable applications Stretch winding Agricultural application Food packaging
Forms	Particle
Processing Method	Blow film Wire & Cable Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.918	g/cm³	ISO 1183/A, ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238, ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	49		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield, molding	12.0	MPa	ASTM D638
Fracture, molding	19.0	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield, molding	17	%	ASTM D638
Fracture, molding	830	%	ASTM D638
Flexural Modulus - 1% Secant (Compression Molded)	256	MPa	ASTM D790

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
Tensile Modulus			ISO 527-3
MD : 50 µm, blown film	160	MPa	ISO 527-3
TD : 50 µm, blown film	180	MPa	ISO 527-3
Tensile Stress			ISO 527-3
MD : Yield, 50 µm, blown film	11.0	MPa	ISO 527-3
TD : Yield, 50 µm, blown film	11.0	MPa	ISO 527-3
MD : 50 µm, blown film	30.0	MPa	ISO 527-3
TD : 50 µm, blown film	37.0	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Broken, 50 µm, blown film	700	%	ISO 527-3
TD : Broken, 50 µm, blown film	850	%	ISO 527-3

Impact	Nominal Value	Unit	Test Method
Impact Strength - Blown Film (50.0 µm)	220	J/cm	ASTM D4272

Additional Information	Nominal Value	Unit	Test Method
Puncture Resistance - Blown Film (50.0 µm)	630	J/m	Internal method
Tear Strength ¹			ISO 6383-2
MD : 50.0 µm	40.0	kN/m	ISO 6383-2
TD : 50.0 µm	120.0	kN/m	ISO 6383-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	100	°C	ISO 306/A
Melting Temperature (DSC)	121	°C	Internal method

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	7.0E+15	ohms·cm	ASTM D257
Dielectric Strength ²	52	kV/mm	ASTM D149
Dielectric Constant (60 Hz)	2.17		ASTM D150
Dissipation Factor (60 Hz)	5.0E-4		ASTM D150

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 50.0 µm, Blown Film)	50		ASTM D2457
Haze (50.0 µm, Blown Film)	13	%	ASTM D1003A

Additional Information	Nominal Value	Unit	Test Method
Blown Film:Film of 50 µm and BUR=2 has been produced on Kiefel IBC with 140 kg/h. Die size 200 mm, die gap 2,7 mm.

Note Message
1 .	Blown Film
2 .	500 V/sec

Resin Grade	Manufacturer	Category	Trademark
CALP VA001	Lion Idemitsu Composites Co., Ltd.	LLDPE	CALP
CP PRYME® Polypropylene PPC100NB-10M	Chase Plastics Services Inc.	PP Copolymer	CP PRYME® Polypropylene
HOPELEX PCH-2002	Lotte Chemical Corporation	PC	HOPELEX
Sylvin 4260-55 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Durethan® BM 25 FN20 DUS013 000000	LANXESS GmbH	Nylon 6	Durethan®