Milastomer™ 8030NHS
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | Milastomer™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pAOw8a_Milastomer-8030NHS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Milastomer™8030NHS is a thermoplastic vulcanized rubber (TPV) material,. This product is available in North America and is processed by extrusion or calendering. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 9.3 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 48 | ||
| Shaw A | 88 | ISO 48 | |
| Shaw A, 5 seconds | 84 | ISO 48 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 4.60 | MPa | ISO 37 |
| Tensile Stress 2(Break) | 8.10 | MPa | ISO 37 |
| Tensile Elongation 3(Break) | 520 | % | ISO 37 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | Internal method |
| Additional Information |
|---|
| All tests performed according to Mitsui methods. |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1970 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Matrixx FPP1A20CC | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Thermoset Plastics DC-151 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| DJSilicone NE--T-2/NE-T-2U (standard) | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| GAPEX® RPP20EA90NA | Ferro Corporation | PP Homopolymer | GAPEX® |