Fiberfil® J-60/40/E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pACR7l_Fiberfil-J-60-40-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil® J-60/40/E is a Polypropylene Homopolymer (PP Homopolymer) material filled with 40% glass fiber. It is available in North America. Important attributes of Fiberfil® J-60/40/E are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.20 | % | |
| 6.35 mm | 0.30 | % | |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 95.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 6000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 157 | °C | |
| 1.8 MPa, Unannealed | 152 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zelux® CN-SS | Westlake Plastics Company | PC | Zelux® |
| AIE PA6 50G3ST | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |
| Globalprene® 3411F | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Sylvin 8925-80 NATURAL | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Abstron KU602M | Bhansali Engineering Polymers Limited | ABS | Abstron |