VERSIFY™ 4200
| Category: | POP , Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | VERSIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p92v0l_VERSIFY-4200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VERSIFY™ 4200 Plastomer is a resin with a medium melt flow rate, therefore making it a general purpose resin. It is suitable for fiber extrusion, extrusion coating, compounding and injection molding processes and applications. It has excellent compatibility with PP and is an useful agent to bring softness and temperature performance. Main Characteristics
Applications
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.876 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Total Crystallinity | 29 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1 | ASTM D2240 | ||
| Shore A, Compression Molded | 94 | ||
| Shore D, Compression Molded | 42 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 22.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 850 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 112 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -23.0 | °C | Internal Method |
| Vicat Softening Temperature | 61.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 84.0 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 20°, 1000 µm, Compression Molded | 127 | ||
| 60°, 1000 µm, Compression Molded | 134 | ||
| Haze (2000 µm, Injection Molded) | 5.1 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Hardness after 10 seconds. |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 1718-FP HO | LyondellBasell Industries | Polyolefin, Unspecified | SEQUEL® |
| Tectron H2244 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Sylvin 8315-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NANCAR® 1053 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| LUVOCOM® 1-8068/GY-HI | LEHVOSS Group | Nylon 66 | LUVOCOM® |