Hanwha Total PE 530G
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p8y06z_Hanwha-Total-PE-530G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 530G is a low-density polyethylene resin for general purpose films. This grade is designed to be processed in conventional blown film equipment. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 12.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 40 µm | 22.6 | MPa | ASTM D882 |
| TD : Break, 40 µm | 15.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm | 240 | % | ASTM D882 |
| TD : Break, 40 µm | 590 | % | ASTM D882 |
| Dart Drop Impact (40 µm) | 65 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| Melting Temperature | 113 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (40.0 µm) | 7.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Blocking, SAMSUNG TOTAL: 240 g/10cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 - 180 | °C | |
| Cylinder Zone 2 Temp. | 160 - 180 | °C | |
| Cylinder Zone 3 Temp. | 160 - 180 | °C | |
| Cylinder Zone 4 Temp. | 160 - 180 | °C | |
| Cylinder Zone 5 Temp. | 160 - 180 | °C | |
| Die Temperature | 160 - 180 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 1 to 2 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycal™ 1850L3H | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| Hax™ HF 22G | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| PELPRENE™ S3001 | TOYOBO America, Inc. | TPEE | PELPRENE™ |
| PERCOM® KHT10 | A. Schulman Europe | PP Homopolymer | PERCOM® |
| Sylvin 2990-76 Blue 8474 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |