POLYLAC® PA-737 A03
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p7mtpF_POLYLAC-PA-737-A03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| White (Similar to RAL 9003), High flow, Medium impact |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 38.0 | MPa | |
| Break | 31.0 | MPa | |
| Tensile Strain (Break) | 20 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1900 | MPa | ISO 178 |
| Flexural Stress 2 | 59.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 19 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ISO 306/A50 |
| -- | 97.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 321S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| NuSil CV-2948 | NuSil Technology | Silicone | NuSil |
| Bergamid™ NI-15GF/000 FR GR002 | PolyOne Corporation | Nylon 610 | Bergamid™ |
| LNP™ LUBRILOY™ D2000P compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |
| LNP™ LUBRICOMP™ ML004LS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ LUBRICOMP™ |