SKYGREEN® JN200
| Category: | PCTG , Polycyclohexylenedimethylene Terephthalate, Glycol |
| Manufacturer: | SK Chemicals |
| Trademark: | SKYGREEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p6DmpV_SKYGREEN-JN200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SKYGREEN® JN200 is a Polycyclohexylenedimethylene Terephthalate, Glycol (PCTG) material. It is available in Asia Pacific, Europe, or North America. Primary attribute of SKYGREEN® JN200: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 45.0 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Break 2 | 53.0 | MPa | ASTM D638 |
| Break | 53.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 4 | 340 | % | ASTM D638 |
| Break | 340 | % | ISO 527-2/50 |
| Flexural Modulus 5 | 1800 | MPa | ASTM D790, ISO 178 |
| Flexural Strength 6 | 67.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | No Break | ASTM D256 | |
| 23°C | 130 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Unannealed | 62.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP H1615 | LG Chem Ltd. | PP Homopolymer | SEETEC PP |
| Sinvicomp SGH9500D | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| VINIKA® CB88EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| TECACOMP® PA66 GF25 TF10 HI natural 9173 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| Kinta FR6600 | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 66 | Kinta |