SABIC® LDPE HP2023J
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p68Ugq_SABIC-LDPE-HP2023J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRODUCT DESCRIPTION: SABIC® LDPE HP2023J is a Low Density Polyethylene grade formulated with slip and anti-block additives. It typically exhibits better draw down ability with high output. Films typically have good optics with low friction and low blocking. TYPICAL APPLICATIONS: Thin shrink film, lamination film, packaging films for food and industrial goods, bags & pouches. It also enables high speed converting without sticking. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (0.0500 mm) | 260 | MPa | ISO 527-2 |
| Tensile Stress (yield, 0.0500mm) | 11.0 | MPa | ISO 527-2 |
| Coefficient of Friction | % | ISO 8295 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 20 - 60 micron | ||
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 21.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 250 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 110 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 111 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 50 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 100 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 9.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Measured on 50 micron thickness blown film extruded at melt temperature of 180°C with BUR of 2.5 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 7200 | POLY GIN | PC+ABS | MARCOBLEND |
| 4MID® 9A22140 HR | 4Plas | Nylon 66 | 4MID® |
| EVICOM™ GD1/881 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| PIVINEL™ 116-R7-LF PROFIL | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| ARLEN™ C430N | Mitsui Chemicals, Inc. | Nylon 6T | ARLEN™ |