LNP™ THERMOCOMP™ RF0069SZ compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p64O79_LNPTHERMOCOMPRF0069SZcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF0069SZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of th is grade include: Flame Retardant, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1006 FR-1 HS Product reorder name: RF0069SZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.67 | g/cm³ | ASTM D792 |
| -- | 1.66 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.0 - 3.0 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.79 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12800 | MPa | ASTM D638 |
| -- | 12800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 157 | MPa | ASTM D638 |
| Fracture | 157 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.0 | % | ASTM D638 |
| Fracture | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 11400 | MPa | ASTM D790 |
| -- 5 | 11000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 217 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 221 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 67 | J/m | ASTM D256 |
| 23°C 7 | 6.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 640 | J/m | ASTM D4812 |
| 23°C 8 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.80 | J | ASTM D3763 |
| -- | 1.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 246 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 9 | 246 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 231 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 227 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 5.3E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 2180 | RTP Company | PEI | RTP |
| RAMTAL PM3009G4 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| TEKAMID™ H14ST | Mando Advanced Materials Co., Ltd. | ABS+Nylon | TEKAMID™ |
| China PPS hx | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Petlon Prime A1-00-00-BK | Petlon Polymers Ltd | Nylon 66 | Petlon Prime |