DAI-EL™ LT-303
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | DAIKIN AMERICA, INC. |
| Trademark: | DAI-EL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p5mbq8_DAI-EL-LT-303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DAI-EL LT-303 is a terpolymer suitable for various peroxide cure systems. LT-303 can be formulated to eliminate the post cure process. LT-303 is designed for transfer and compression molding applications that require a balance between good low temperature flexibility and high elongation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.79 | g/cm³ | ASTM D792 |
| Mooney Viscosity (ML 1+10, 121°C) | 25 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 69 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 2.60 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 18.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 350 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 25 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ASTM D573 | ||
| 200°C, 70 hr | -1.0 | % | ASTM D573 |
| 230°C, 70 hr | -15 | % | ASTM D573 |
| Change in Ultimate Elongation in Air | ASTM D573 | ||
| 200°C, 70 hr | -10 | % | ASTM D573 |
| 230°C, 70 hr | -9.0 | % | ASTM D573 |
| Change in Durometer Hardness in Air | ASTM D573 | ||
| Support a, 200°C, 70 hr | 2.0 | ASTM D573 | |
| Support a, 230°C, 70 hr | 1.0 | ASTM D573 |
| Additional Information |
|---|
| All tests performed were performed under DAIKIN test methodsFluorine Content: 65%Curing characteristic, Measuring Temperature: 160°CCuring characteristic, Curelastomer: 2.3 minCuring characteristic, Measuring Temperature: 177°CCuring characteristic, Curelastomer: 0.8 minTR test, TR10: -32°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6870 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| NuSil MED-1131 | NuSil Technology | Silicone | NuSil |
| Epoxies, Ect. 40-3909 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Lupoy® GN5201F | LG Chem Ltd. | PC+ABS | Lupoy® |
| Durethan® BKV 140 H2.0 DUS008 900051 | LANXESS GmbH | Nylon 6 | Durethan® |