Ultramid® 8272G HS BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p3HYdn_Ultramid-8272G-HS-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, PA6 blow molding compound offering an excellent balance of engineering properties combined with the melt strength ideally suited for blow molding and other applications requiring ultra high melt viscosity. It exhibits improved strength, stiffness and creep resistance compare to standard blow molding grades. Outstanding permeability and chemical resistance to oils, hydrocarbons and most solvents are other advantages along with excellent stiffness ad the ability to fabricate complex shapes for cost effective metal replacements. Applications Ultramid 8272G HS BK-102 is designed for blow molding applications requiring improved short term thermal performance as well as extrusions. It is ideal for air ducts, reservoirs and covers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.22 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.4 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.4 | -- | % | ISO 62 |
| Saturation | 8.3 | -- | % | ASTM D570 |
| Saturation, 23°C | 8.3 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.3 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -40°C | 6370 | 6400 | MPa | |
| 23°C | 5220 | 3100 | MPa | |
| 80°C | 2100 | 1900 | MPa | |
| 121°C | 1450 | 1500 | MPa | |
| Tensile Strength | ASTM D638, ISO 527-2 | |||
| Break, -40°C | 115 | 110 | MPa | |
| Break, 23°C | 110 | 60.0 | MPa | |
| Break, 121°C | 45.0 | 25.0 | MPa | |
| Tensile Elongation | ||||
| Break, -40°C | 2.0 | 2.0 | % | ASTM D638 |
| Break, 23°C | 3.0 | -- | % | ASTM D638, ISO 527-2 |
| Break, 121°C | 15 | 20 | % | ASTM D638 |
| Flexural Modulus | ||||
| -40°C | 5200 | 5580 | MPa | ASTM D790 |
| 23°C | 4650 | 1970 | MPa | ASTM D790 |
| 121°C | 995 | -- | MPa | ASTM D790 |
| 23°C | 4300 | -- | MPa | ISO 178 |
| Flexural Strength | ASTM D790 | |||
| -40°C | 200 | 265 | MPa | |
| 23°C | 165 | 80.0 | MPa | |
| 121°C | 50.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.1 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact | ||||
| -40°C | 40 | 40 | J/m | ASTM D256 |
| 23°C | 45 | 160 | J/m | ASTM D256 |
| 23°C | 5.9 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 197 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 170 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 9.7E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 2.8E-5 | -- | cm/cm/°C | |
| Transverse | 7.2E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | > 1.0E+13 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | > 1.0E+13 | ohms·cm | IEC 60093 |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Blow Molding Drying Temperature | 80 | -- | °C | |
| Blow Molding Drying Time | 2.0 to 4.0 | -- | hr | |
| Blow Molding Melt Temperature | 245 to 260 | -- | °C | |
| Blow Molding Moisture Content | < 0.15 | -- | % | |
| Blow Molding Mold Temperature | 60 | -- | °C | |
| Blow-up Ratio | 2.0:1.0 | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S-RIM™ 7241 Tan | Hapco Inc. | TP, Unspecified | S-RIM™ |
| Torlon® AI-10 | Solvay Specialty Polymers | PAI | Torlon® |
| Bergamid™ A700 G25 U GR037 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Hylon® N2023STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Pibiter® NRV10 NATURALE | SO.F.TER. SPA | PBT | Pibiter® |