BLUESTAR® POM BS090
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Beijing Ranger Chemical Co., Ltd. |
| Trademark: | BLUESTAR® POM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p1LqOv_BLUESTARPOMBS090.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BLUESTAR®POM BS090 is a polyoxymethylene (POM) copolymer product,. It is available in North America, Europe or Asia Pacific. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.8 - 2.2 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2450 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 62.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 42 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESN Noir P40 TL | Arkema | Nylon 11 | Rilsan® |
| TEDUR® L 9510-1 | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| KIBITON® TPE PB-5502 | CHI MEI CORPORATION | TPE | KIBITON® TPE |
| Monprene® CP-32263 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| MAXAMID™ RC6G30HSL-BK09 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |