AURUM® PI-PA
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | Mitsui Chemicals, Inc. |
| Trademark: | AURUM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | p01xbz_AURUMPIPA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AURUM ® PIPA exhibits a glass transition temperature of 258°C and has higher heat resistance than that of the standard AURUM ® resins (glass transition temperature: 250°C). AURUM ® PI-PA shows better extrudability than that of the standard AURUM ® resins and is suitable for the manufacture of stock shapes. Because of its low rate of crystallization, AURUM ® PI-PA is practically non-crystalline. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (400°C/1.05 kg) | 8.0 | g/10 min |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | 95.0 | MPa | |
| Tensile Elongation (Break) | 82 | % | |
| Flexural Modulus | 3030 | MPa |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 258 | °C | |
| Melting Temperature | 380 | °C | |
| Peak Crystallization Temperature (DSC) | 320 | °C |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Crystallization Rate - (t1/2min) | 100 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 380 - 420 | °C | |
| Mold Temperature | 180 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| mPact™ D350 | Chevron Phillips Chemical Company LLC | mLLDPE | mPact™ |
| Akulon® Ultraflow K-FG3 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| Fainplast PVC CKL 0221/T | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| KPOL-PP K-PPH 14.0 | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| Moplen EP440G | LyondellBasell Industries | PP, HMS | Moplen |