PBT, 12 % glass fibers, injection molding, flame retardant

General Information
Filler / Reinforcement	Glass fiber reinforced material, 12% filler by weight
Additive	Flame retardancy
Features	Flame retardancy
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.53	g/cm³	ISO 1183
Apparent Density	0.80	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)	21.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 2577
Vertical flow direction : 250°C, 2.00mm ¹	1.1	%	ISO 2577
Vertical flow direction : 120°C, 4 hours, 2.00mm ²	0.10	%	ISO 2577
Flow direction : 250°C, 2.00mm ³	0.80	%	ISO 2577
Flow direction : 120°C, 4 hours, 2.00mm ⁴	0.10	%	ISO 2577
Water Absorption			ISO 62
Saturated, 23°C	0.30	%	ISO 62
Equilibrium, 23°C, 50% RH	0.10	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	180	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	6000	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	100	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	2.5	%	ISO 527-2/5
Tensile Creep Modulus			ISO 899-1
1 hr	5500	MPa	ISO 899-1
1000 hr	5000	MPa	ISO 899-1
Flexural Modulus ⁵(23°C)	5700	MPa	ISO 178/A
Flexural Stress ⁶(23°C)	155	MPa	ISO 178/A
Flexural Strain at Flexural Strength (23°C) ⁷	3.2	%	ISO 178/A

Thermal	Nominal Value	Unit	Test Method
Halving Interval			IEC 60216
Electric Strength	12.4	°C	IEC 60216
Tensile Impact Strength	9.2	°C	IEC 60216
Tensile Strength	11.7	°C	IEC 60216
Temperature index			IEC 60216
Electric Strength, 20000 hr	145	°C	IEC 60216
Tensile Impact Strength, 20000 hr	135	°C	IEC 60216
Tensile Strength, 20000 hr	140	°C	IEC 60216

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion (23°C)	A 1		IEC 60426
ISO Shortname	PBT, GFHMR, 09-060, GF12; ISO 1043-PBT GF FR (17)		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 - 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	< 10	kJ/m²	ISO 179/1eA
23°C	< 10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	25	kJ/m²	ISO 179/1eU
23°C	25	kJ/m²	ISO 179/1eU
Notched Izod Impact			ISO 180/1A
-40°C	< 10	kJ/m²	ISO 180/1A
-30°C	< 10	kJ/m²	ISO 180/1A
23°C	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	20	kJ/m²	ISO 180/1U
23°C	20	kJ/m²	ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	210	°C	ISO 75-2/B
1.8 MPa, not annealed	185	°C	ISO 75-2/A
Vicat Softening Temperature	205	°C	ISO 306/B120
Ball Pressure Test (205°C)	Pass		IEC 60695-10-2
Melting Temperature ⁸	225	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 55°C	4.0E-5	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.0E-4	cm/cm/°C	ISO 11359-2
Thermal Conductivity (23°C)	0.20	W/m/K	ISO 8302
RTI Elec	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI	140	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity (23°C)	> 1.0E+13	ohms·cm	IEC 60093
Dielectric Strength (23°C, 1.00 mm)	29	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	3.60		IEC 60250
23°C, 1 MHz	3.40		IEC 60250
Dissipation Factor			IEC 60250
23°C, 100 Hz	4.0E-3		IEC 60250
23°C, 1 MHz	0.019		IEC 60250
Comparative Tracking Index (CTI)	PLC 3		UL 746
Comparative Tracking Index (Solution A)	200	V	IEC 60112
High Amp Arc Ignition (HAI)	PLC 0 PLC 0 PLC 0		UL 746
Hot-wire Ignition (HWI)	PLC 2 PLC 3 PLC 4		UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.400 mm)	V-0		UL 94
Glow Wire Flammability Index			IEC 60695-2-12
0.800 mm	960	°C	IEC 60695-2-12
1.50 mm	960	°C	IEC 60695-2-12
3.00 mm	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature			IEC 60695-2-13
0.750 mm	700	°C	IEC 60695-2-13
1.50 mm	700	°C	IEC 60695-2-13
3.00 mm	700	°C	IEC 60695-2-13
Oxygen Index ⁹	32	%	ISO 4589-2

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 - 8.0	hr
Processing (Melt) Temp	240 - 260	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2mm, 80°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 80°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	10°C/min
9 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
Telcar® TL-1336B	Teknor Apex Company	TPE	Telcar®
VITAMIDE® TH36BK6752	Jackdaw Polymers	Nylon 66/6	VITAMIDE®
Elvax® 3135X	DuPont Packaging & Industrial Polymers	EVA	Elvax®
KumhoSunny AES HW600G	Shanghai KumhoSunny Plastics Co., Ltd.	AES	KumhoSunny AES
Polene LDPE D 2024	TPI Polene Public Company Limited	LDPE	Polene LDPE