| Feather Lite® is a heavily filled low-density urethane casting resin. Cured plastic is lightweight (it floats in water!) and has a much lower density than other casting resins. Feather Lite® features a convenient 1A:1B by volume mix ratio and mixes easily (pre-mixing of parts A & B is necessary). Cured plastic is strong and can be carved, machined, drilled, sanded, etc. Feather Lite® can be pigmented with SO-Strong® color tints prior to casting and finished castings can be painted. And because this product is low-density, it yields more plastic per pound/kg. than other casting resins, the cost per casting is low. Feather Lite® can be used for a variety of art or industrial design related applications including reproducing sculpture, making fishing lures, prototype model making, casting doll heads and figures, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.668 | g/cm³ | ASTM D1475 |
| Specific Volume | 1.49 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 1A:1B by volume or weight |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.30 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 58 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1080 | MPa | ASTM D638 |
| Tensile Strength (Break) | 14.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638 |
| Flexural Modulus | 1130 | MPa | ASTM D790 |
| Flexural Strength | 23.7 | MPa | ASTM D790 |
| Compressive Modulus | 370 | MPa | ASTM D695 |
| Compressive Strength | 21.2 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life | 8.5 | min | |
| Thermoset Mix Viscosity | 410 | cP | ASTM D2393 |
| Demold Time | 120 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 400 GB 20 | RTP Company | PS (GPPS) | RTP |
| Nypol® PA B3 G10 BRC0003 NT386 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| ESPOLEX 412A | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| Hylon® N2033TL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Sylvin 2985-78 Clear Green 3202 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |