Witcom PBT 6G-EC
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oz2eii_Witcom-PBT-6G-EC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PBT 6G-EC is a polybutene terephthalate (PBT) product, which contains a 30% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.30 - 0.50 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 - 2.0 | % | ISO 527-2 |
| Flexural Modulus | 9000 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 7.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | °C | ISO 75-2/A |
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 100 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIEL® 5720 | Samyang Corporation | TPEE | TRIEL® |
| BMC 3001H | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Anjacom® 55/80-GK10 | Almaak International GmbH | PC+ABS | Anjacom® |
| HAIPLEN H90 T4 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| LNP™ THERMOCOMP™ RZ0069 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |