Karina BLACK PVC COMPOUND 807D48/ 1-C-IS-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oyzXbN_Karina-BLACK-PVC-COMPOUND-807D48-1-C-IS-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND CLASS 70C (ST1) RECOMMENDED FOR ELECTRICAL FLEXIBLE CABLES JACKETING. ALSO SUITABLE FOR INJECTION OF PLUG. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.33 to 1.39 | g/cm³ | IEC 60811-1-3 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -0.870 to 0.730 | ME 12 | |
| Color b | -1.32 to 0.280 | ME 12 | |
| Color L | 26.2 to 27.8 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 78 to 82 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -26.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+13 | ohms·cm | NBR 5403 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1500-72D TFE 15 | RTP Company | TEEE | RTP |
| Next Nylon 66 Prime Series PG15-01ABK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| ADDINYL A2 G30 | ADDIPLAST | Nylon 66 | ADDINYL |
| Elastron® V V250.A65.B | Elastron USA, Inc. | TPV | Elastron® V |
| Hapflex™ 561-6 | Hapco Inc. | TP, Unspecified | Hapflex™ |