LNP™ STAT-LOY™ A3000TXB compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oyUtRK_LNP-STAT-LOY-A3000TXB-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY A3000TXB is a compound based on ABS resin. Added features of this material include: Antistatic, Transparent. Bioassessed to ISO 10993. Also known as: LNP* STAT-LOY* Compound A3000TXB Product reorder name: A3000TXB |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.09 | g/cm³ | |
| -- | 1.08 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.60 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.54 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.81 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1660 | MPa | ASTM D638 |
| -- | 1550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 38.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/5 |
| Break 3 | 27.0 | MPa | ASTM D638 |
| Break | 26.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/5 |
| Break 5 | 31 | % | ASTM D638 |
| Break | 29 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1630 | MPa | ASTM D790 |
| -- 7 | 1500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 49.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 54.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 9 | 15 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 20.0 | J | ASTM D3763 |
| -- | 33.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 78.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 77.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 66.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 66.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.0E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+10 to 1.0E+12 | ohms·cm | ASTM D257 |
| Static Decay 12 | < 1.0 | sec | FTMS 101B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| 12 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9459-73 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| VENYL UG500 | AD majoris | Nylon 66 | VENYL |
| Wellamid® MRT1487 BK | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| EPLAMID 6 GFR 30 NC ST | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| Sylvin 9604-95C CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |