Niuk YPC5008
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Shanghai Niuk New Plastic Technology Co., Ltd. |
| Trademark: | Niuk |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | owNvwe_Niuk-YPC5008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Niuk YPC5008 is an Acetal (POM) Copolymer material filled with 20% glass fiber. It is available in Asia Pacific. Primary attribute of Niuk YPC5008: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 to 0.90 | % | ISO 2577 |
| Ash Content | 20 | % | ISO 3451 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | 160 | °C | ISO 75-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 105 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 to 5.0 | % | ISO 527-2 |
| Flexural Modulus | 6400 | MPa | ISO 178 |
| Flexural Stress | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 62 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 155 | °C | ISO 306 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GTPO8290FR-75 RoHS | S&E Specialty Polymers, LLC | TPO (POE) | S&E Wire & Cable |
| SEPAZ™ LC30 | Mando Advanced Materials Co., Ltd. | PP Copolymer | SEPAZ™ |
| HiFill® PA6 0266 B | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Leona™ 53G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| LNP™ THERMOCOMP™ PF002 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |